HOT ROLLED STEEL GRADES FOR STRUCUTRAL PURPOSES (EN 10025-2)
Gli acciai di questa gamma, non legati, vengono definiti principalmente per il carico di snervamento minimo garantito. La lettera S che precede la parte numerica ne indica l’impiego in ambito strutturale (costruzioni, gallerie, ecc.)
Grade technical data This range of grades, not alloyed, are mainly defined by the minimum yield strength thy must achieve. The letter S which comes first in the name means it is to be used for structural purposes (buildings, tunnelling etc).
Chemical Composition – cast analysis for product thickness ≤ 40 mm (EN 10219)
| Nome Steel name |
Numero Number |
Deossidazione De-Oxidation |
% C | % SI | % MN | % P | % S | % N |
|---|---|---|---|---|---|---|---|---|
| S235JRH | 1.0039 | FF | 0,17 | – | 1,40 | 0,040 | 0,040 | 0,009 |
| S275JOH | 1.0149 | FF | 0,20 | – | 1,50 | 0,035 | 0,035 | 0,009 |
| S275J2H | 1.0138 | FF | 0,20 | – | 1,50 | 0,030 | 0,030 | – |
| S355J0H | 1.0547 | FF | 0,22 | 0,55 | 1,60 | 0,035 | 0,035 | 0,009 |
| S355J2H | 1.0576 | FF | 0,22 | 0,55 | 1,60 | 0,030 | 0,030 | – |
La lettera maiuscola S indica acciaio per impieghi strutturali Il numero che segue indica il carico unitario di snervamento minimo prescritto per spessori non superiori a 16 mm La sigla J2 indica le caratteristiche di resistenza a -20°C di minimo 27 Joule La sigla J0 indica le caratteristiche di resistenza a 0°C di minimo 27 Joule La sigla JR indica le caratteristiche di resistenza a +20°C di minimo 27 Joule La lettera H indica il profilo cavo.
Capital letter S means steel for structural purpose The following number indicates the minimum unitary loading yield strength for thicknesses under 16mm The acronym J2 indicates the resilience features at a temperature of -20°C of minimum 27 Joules The acronym J0 indicates the resilience features at a temperature of 0°C of minimum 27 Joules The acronym JR indicates the resilience features at a temperature of +20°C of minimum 27 Joules Letter H means hollow section.
Mechanical Properties of hollow s ections in thicknesses ≤ 40 mm (EN10219)
| Nome Steel name |
Numero Number |
Snervamento min min yield ReH (MPa) |
Rottura tensile Rm (MPa) |
Allungamento min Elongation min A % |
Resilienza min Min impact energy KV (J) |
||||
|---|---|---|---|---|---|---|---|---|---|
| ≤ 16 | >16≤40 | <3 | ≥3≤40 | ≤40 | -20°C | 0°C | +20°C | ||
| S235JRH | 1.0039 | 235 | 225 | 360-510 | 360-510 | 24 | – | – | 27 |
| S275JOH | 1.0149 | 275 | 265 | 430-580 | 410-560 | 20 | – | 27 | – |
| S275J2H | 1.0138 | 27 | – | – | |||||
| S355J0H | 1.0547 | 355 | 345 | 510-680 | 470-630 | 20 | – | 27 | – |
| S355J2H | 1.0576 | 27 | – | – |