ALLOY 600 – BARS

Download
Applications

INDUSTRIAL

Industrial Furnaces, Reaction Vessels and Heat Exchanger, High Temperature Sensors, ect.

Chemical Composition (Nominal) %
Element Percentage (%)
Ni (Nickel) 72.0 min
Cr (Chromium) 14.0 – 17.0
Fe (Iron) 6.0 – 10.0
Mn (Manganese) 1.0 max
C (Carbon) 0.15 max
Cu (Copper) 0.5 max
Si (Silicon) 0.5 max
S (Sulfur) 0.015 max
Features
  • Good resistance against oxidation, carbonization and nitriding
  • Good resistance to stress corrosion in room and increased temperatures
  • Good resistance against dry chlorine and hydrogen chloride
  • Good mechanical properties at both low and high temperatures
Physical Properties
Density 8.5 g/cm³ at 20°C

 

Standard

ASTM B166

Material

INCONEL 600 / UNS N06600 / 2.4816

Mechanical Properties
Heat Treatment Tensile Strength

min, psi (MPa)

 Yield Strength

min, (0.2% offset)

psi (MPa)

 Elongation

in 2 in. or 50 mm

(or 4 D), min, %
Cold-worked (as-worked): Rounds: Under 1/2 120,000 (825) 90,000 (620) 7
Cold-worked (as-worked): Rounds: 1/2 to 1 110,000 (760) 85,000 (585) 10
Cold-worked (as-worked): Rounds: over 1 to 2 1/2 105,000 (725) 80,000 (550) 12
Hot-worked (as-worked): Rounds: 1/4 to 1/2 95,000 (655) 45,000 (310) 20
Hot-worked (as-worked): Rounds: over 1/2 to 3 90,000 (620) 40,000 (275) 25
Surface

Bright annealed / annealed

Package

Wooden case

Heat Treatment

Soft Annealing / Solution Annealing

Soft annealing of Alloy 600 should take place in the temperature range between 920 and 1,000°C (1,688 and 1,832°F).

Solution annealing of Alloy 600 H should take place at temperatures between 1,080 and 1,150°C (1,976 and 2,102°F).